无黏土相盐水储层钻开液体系构建及其抗污染性能评价

采用NaCl/KCl/HCOONa复配欠饱和盐水作为钻开液的基础液相,自研的聚合物VIS-B作为流型调节剂,可酸溶的改性淀粉STA作为体系的降失水剂,Dua及Jqw作为暂堵材料,构建了一套无黏土相钻开液体系。该体系在密度1.10~1.28 g/cm^3间稳定可调,抗温可达130℃,具有较高的低剪切速率黏度和较好的润滑性能,且能有效抵抗各类储层污染物的污染,满足了Missan油田不同储层段的作业需求。     

Evolution of precursor powders prepared by oxalate freeze drying towards high performance Bi-2212 wires

Bi₂Sr₂CaCu₂O_x (Bi-2212) precursor powders were synthesized by the oxalate freeze drying (OFD) method. In comparison with the traditional method, the novel method could shorten the processing steps and thus improve the fabrication efficiency of precursor powder. The phase, microstructure and superconducting properties of Bi-2212 precursor powders and wires were characterized by X-ray diffraction, scanning electron microscopy and four-probe method, respectively. The thermal behavior, surface area and particle size of powders were also discussed. The results indicated that large surface area and small particle size might improve the reactivity and uniformity of powders. These properties were beneficial for the rapid and homogeneous formation of Bi-2212. High-purity crystallized Bi-2212 powders without Bi-2201 and alkaline-earth cuprates phases could be achieved. Furthermore, multi-filamentary Bi-2212 wires with OFD powders showed good microstructures without noticeable pores and large secondary particles. Therefore, high engineering critical current densities (J_e) of 1619 A/mm² and critical current densities (J_c) of 7039 A/mm² were obtained in Bi-2212 wires at 4.2K, self field. It indicated that the oxalate freeze drying method would be a potential candidate for the mass production of high performance Bi-2212 wires.     

High energy storage and ultrafast discharge in NaNbO3-based lead-free dielectric capacitors via a relaxor strategy

Dielectric capacitors with decent energy storage and fast charge-discharge performances are essential in advanced pulsed power systems. In this study, novel ceramics (1-x)NaNbO₃-xBi(Ni_2/3Nb_1/3)O₃(xBNN, x = 0.05, 0.1, 0.15 and 0.20) with high energy storage capability, large power density and ultrafast discharge speed were designed and prepared. The impedance analysis proves that the introducing an appropriate amount of Bi(Ni_0·5Nb_0.5)O₃ boosts the insulation ability, thus obtaining a high breakdown strength (E_b) of 440 kV/cm in xBNN ceramics. A high energy storage density (W_total) of 4.09 J/cm³, recoverable energy storage density (W_rec) of 3.31 J/cm³, and efficiency (η) of 80.9% were attained in the 0.15BNN ceramics. Furthermore, frequency and temperature stability (fluctuations of W_rec ≤ 0.4% over 5–100 Hz and W_rec ≤ 12.3% over 20–120 °C) were also observed. The 0.15BNN ceramics exhibited a large power density (19 MW/cm³) and ultrafast discharge time (~37 ns) over the range of ambient temperature to 120 °C. These enhanced performances may be attributed to the improved breakdown strength and relaxor behavior through the incorporation of BNN. In conclusion, these findings indicate that 0.15BNN ceramics may serve as promising materials for pulsed power systems.     

Influence of Sr ions on the structure and dielectric properties of Cu/Nb Co-doped BaTiO3 ceramics

Sr-modified Cu/Nb co-doped BaTiO₃ ceramics were prepared using solid-state reactions and the structures and dielectric properties were studied. All the samples had single-phase perovskite structures with no detectable secondary phases. In the low-temperature range, the dielectric constant decreased as the Sr content increased in the high- and low-frequency ranges. Two dielectric constant plateaus accompanied by dielectric relaxation peaks were present in the loss curves, and the relaxation process deviated from the Arrhenius law at low temperatures. The dielectric constants of different plateaus were related to inhomogeneous structures such as grain interiors and grain boundaries. The polarization strength of the grain boundaries in the low-frequency range increased with the temperature and that of the grain interiors demonstrated paraelectric behaviour in high-temperature ranges. An analysis of the electric modulus spectra indicated a close relationship between the relaxation process and resistivity of the grains for high-frequency relaxation. The impedance spectra at high temperatures consist of three electrical responses, corresponding to the effects of grains, grain boundaries, and electrodes. The dielectric relaxation appeared in high temperature range was related to the electrical properties of the grain boundaries.     

Establishment of a color tolerance for yarn-dyed fabrics from different color-depth yarns

Yarn-dyed fabric is often woven from warp and weft yarns in the same color depth to ensure a uniform color appearance. The difference in color depth between warp and weft tends to result in the uneven color of the yarn-dyed fabric. This article aims to establish a color tolerance for yarn-dyed fabric that can be woven with a qualified color appearance but from the warp and weft yarns in different color depths. A total of 27 yarn-dyed fabric samples in three color series (red, yellow, and blue) were evaluated by using the yarn-dyed fabric from warp and weft yarns in the same color depth of 2% (on weight of fabric, owf) as the standard. Visual assessment and instrumental measurement of color were carried out to establish the color tolerance ellipse that was defined as CMC (Color Measurement Committee) color differences (2:1) of no more than 1.00. It was found that the color strengths (K/S) and color differences (ΔE_CMC(2:1)) of these fabric samples for each color series had linear relationships with the color depths of warp and weft yarns. The color tolerance ellipses indicated that, even though the warp and weft yarns had an apparent color difference, they could be woven in fabrics with relatively uniform color appearance and meet the requirements for yarn-dyed fabric. This work provided valuable insight into the production of qualified yarn-dyed fabrics from unqualified dyed yarns.     

黄芩苷印迹聚合物在银黄口服液质量分析中的应用

从天然产物和中草药中选择性提取生物活性化合物是困难的,但对药物分析和新药开发是必要的也是亟需的.该研究采用沉淀聚合法,以黄芩苷为模板分子,与丙烯酰胺和乙二醇甲基丙烯酸共聚,以N、N-二甲基甲酰胺为致孔剂合成了分子印迹聚合物,与非印迹聚合物相比,制备的分子印迹聚合物具有良好的选择性,并用于银黄口服液的质量分析.结果表明:该分子印迹聚合物能从复杂基质中选择性提取黄芩苷及其结构类似物.     

Novel silicon-contained lignin-based carbon fibers derived from bamboo pulping black liquor with improved electrochemical performance for supercapacitors

Carbon fibers (CFs) are a promising candidate as electrode materials for flexible supercapacitors given its light weight and moderate cost. In this study, the lignin used was partially separated from kraft bamboo pulping black liquor and the higher molecular weight fraction, unavoidably contains a small amount of silicon compounds, so named silicon-contained lignin. Novel CFs were prepared using commercial polyacrylonitrile (PAN) and the lignin by electrospinning and further carbonization. Even in the presence of silicon compounds, the fibrous morphology of precursor fibers was significantly good, and the CFs with uniform fiber diameter and high specific surface area up to 182 m²/g were obtained with an increase in silicon-contained lignin. The CFs fabricated from silicon-contained lignin and commercial PAN had higher specific capacitance (22.20 mF/cm² at 10 mA/cm²) and superb cycling stability (94.21%) than that from silicon-free lignin or pure PAN separately.     

Modification of the wood-plastic composite for enhancement of formaldehyde clearance and the 3D printing application

As the formaldehyde is one of the main indoor pollutants, the purpose of this study is to effectively remove indoor formaldehyde pollution by using environmentally friendly 3D printing ornaments. The wood 3D printing filaments cellulose/polylactic acid composite (Cellu/P) was selected as the starting material, and 3-aminopropyltriethoxysilane (APTES) was used for chemical modification to obtain a series of cellulose composite materials with amino groups. The modified composite materials (APTES@Cellu/P) were characterized by Fourier transform infrared, X-ray diffraction, scanning electron microscope, energy dispersive spectroscopy, thermogravimetric analysis, and mechanical tests, and a formaldehyde removal experiment was performed. The feasibility of 3D printing was evaluated, and the process of 3D printing-functionalized customized ornaments was proposed, and then a school emblem was used for modeling, printing, and surface modification. Compared with the commercially traditional activated carbon, 3D printing-customized ornaments of APTES@Cellu/P material has a better formaldehyde removal effect, and can even avoid the secondary pollution that is common to the activated carbon.